Habet quattuor modos producendi: primus instat corona.(Pinis magnetici et tenaces miscentur aequaliter in ratione voluminis circiter 7:3, ad crassitudinem debitam convoluta et postea solidificata ad opus operis conficiendum), secunda iniectio corona est.(Misce magneticum pulverem cum ligante, calore et commisce, prae-granulate, siccitate, et tunc mitte spiralem baculum ad calefactionem cameram calefaciendi, injicias in cavum formae formae, ut opus factum post refrigerationem obtineat); tertium est extrusio coronae.(Similiter idem cum infusione fingendi methodo, sola differentia est, quod post calefactionem, globulos in formam per cavitatem ad coronam continuam extruduntur), et quarta est corona compressionis (Misce magneticum pulverem et ligamen secundum. ratio granulata et quantitatem agentis coeundi addat, in formam premat, ad 120°~ 150° solidatur, ac demum opus operis obtineat).
Incommodum est quod compages NdFeB tarde incipit, et proprietates magneticae infirmae sunt, praeterea gradus applicationis angustus est, et dosis etiam parva est.
Eius commoda alta sunt remanentia, magna vis coactiva, alta vis magneticae industriae, summa operandi ratio dotis, unum tempus sine processus secundario formans, et fieri potest in varias magnetes implicatas, quae magnum volumen et pondus minuere possunt. motor.Et magnetizari potest ad quamlibet partem, quae faciliorem reddere potest productionem multi poli vel etiam infiniti poli altiore magnete.
Maxime adhibetur in officio automationis instrumento, instrumento electrica, instrumento audio-visuali, instrumento, parvis motoribus et machinis metiendis, motoribus telephonicis mobilis vibrationum, magneticis scutulis typographi, instrumenti ferri disci fusi motorum HDD potentia, alia micro DC motorum et instrumentorum automationis.
Characteres magnetici et Physica Bonded NdFeB
Magnetica Characteres et Physica Bonded Compressio Iniectio Cingula NdFeB
| Gradus | SYI-3 | SYI-4 | SYI-5 | SYI-6 | SYl-7 | SYI-6SR(PPS) | ||
| Inductione Residua (mT) (KGs) | 350-450 | 400-500 | 450-550 | 500-600 | 550-650 | 500-600 | ||
| (3.5-4.5) | (4.0-5.0) | (4.5-5.5) | (5.0-6.0) | (5.5-6.5) | (5.0-6.0) | |||
| Coactio vis (KA/m) (KOe) | 200-280 | 240-320 | 280-360 | 320-400 | 344-424 | 320-400 | ||
| (2.5-3.5) | (3.0-4.0) | (3.5-4.5) | (4.0-5.0) | (4.3-5.3) | (4.0-5.0) | |||
| Coactio intrinseca vis (KA/m) (KOe) | 480-680 | 560-720 | 640-800 | 640-800 | 640-800 | 880-1120 | ||
| (6.5-8.5) | (7.0-9.0) | (8.0-10.0) | (8.0-10.0) | (8.0-10.0) | (11.0-14.0) | |||
| Maximilianus.Energy Product (KJ/m3) (MGOe) | 24-32 | 28-36 | 32-48 | 48-56 | 52-60 | 40-48 | ||
| (3.0-4.0) | (3.5-4.5) | (4.5-6.0) | (6.0-7.0) | (6.5-7.5) | (5.0-6.0) | |||
| Permeabilitas (μH/M) | 1.2 | 1.2 | 2.2 | 1.2 | 1.2 | 1.13 | ||
| Tempetraturus Coefficiens (%/℃) | -0.11 | -0.13 | -0.13 | -0.11 | -0.11 | -0.13 | ||
| Curie Temperature (℃) | 320 | 320 | 320 | 320 | 320 | 360 | ||
| Max.Work Temperature (℃) | 120 | 120 | 120 | 120 | 120 | 180 | ||
| Magnetizing Force (KA/m) (KOe) | 1600 | 1600 | 1600 | 1600 | 1600 | 2000 | ||
| 20 | 20 | 20 | 20 | 20 | 25 | |||
| Dendity (g/m3) | 4.5-5.0 | 4.5-5.0 | 4.5-5.1 | 4.7-5.2 | 4.7-5.3 | 4.9-5.4 | ||
Product Feature
NdFeB magnetis lineamenta religata;
1. Res magnae inter magnetem sinteredum NdFeB et magnetem ferritum, est magna effectus magnetis isotropici permanentis cum bona constantia et stabilitate.
2. Possunt fieri magnetes permanentes magnitudinum magnitudinum, figurarum multiplicium et accurationis geometricae altae cum corona et injectione forma pressa.Facilis consequatur magna automated purus.
3. Potest magnetizari per quamlibet partem.Multi poli vel etiam innumerabiles polos nexa NdFeB effici possunt.
4. Magnetes NdFeB bonded late usi sunt in omnibus motoribus microformibus, ut fusum motorem, motorem synchronum, stepper motorem, DC motorem, motorem Brushless, etc.