Applicatio: Late usus est in motore Brushless, magnete permanente motore industriae, motore textili, motore autocineto, magnete permanenti directo motore, motore lineari, aere condicioni motore compressore, instrumento mechanico motore permanenti, marino generante, magnete permanenti generante, magnete permanenti propellente motore. fodienda magnete permanenti, motore coitu, motore chemico magnete permanenti, motore EV, motore sentino, EPS motore, sensori et aliis areae.
Product nativus: magnes omnes nativus, longitudo potest esse ex 0.5mm-200mm, latitudo ab 0.5mm-150mm, crassitudo ab 0.5mm-70mm, quod maxime postulationem clientium occurrere potest.
Coating: NdfeB magnes oxidize facile est, ita normaliter tunica opus est, litura communi usus in foro similis;
1. ZN plating (qualem metalli efficiens, salis aspergine test ad 24-48 horas pervenire potest, princeps sumptus effectus est, ut optimus electio plerisque clientibus est).
2. NICUNI (quadam metallica efficiens, salis imbre experimentum ad 48-72 horas potest, sumptus effectus altior est quam ZN, sed tamen valde late in foro conventus conditio dura est, producto corrosio resistendi requisita emptoris potest. eligere).
3. Epoxy (conductitas non-metallica, conductivity non magnetica, potest reducere damnum currentis torrens motoris, probatio salis imbre 72-96 horas attingere potest, altior sumptus quam ZN NICUNI efficiens).
4. Alia vestis quae etiam usus est: Phosphate, Sn, Au, Ag, Parylene et cetera.
Tolerantia: Plerumque magnes noster tolerantia +/-0.05mm post coatingit.
NdFeB Processus Productio
Introductio coating
Superficies | Coating | Crassitudo μm | Color | SST Horae | PCT Horae | |
Nickel | Ni | 10~20 | Clara Silver | >24~72 | >24~72 | |
Ni+Cu+Ni | ||||||
Nigrum Nickel | Ni+Cu+Ni | 10~20 | Clara Niger | >48~96 | >48 | |
Cr3+Zinc | Zn C-Zn | 5~8 | Bright Blue Lucens Color | >16~48 >36~72 | --- | |
Sn | Ni+Cu+Ni+Sn | 10~25 | Argenti | >36~72 | >48 | |
Au | Ni+Cu+Ni+Au | 10~15 | Aurum | >12 | >48 | |
Ag | Ni+Cu+Ni+Ag | 10~ 15 | Argenti | >12 | >48 | |
Epoxy | Epoxy | 10~20 | Nigrum / Grey | >48 | --- | |
Ni+Cu+Epoxy | 15~30 | >72~108 | --- | |||
Zn+Epoxy | 15~25 | >72~108 | --- | |||
passionem | --- | 1~3 | Griseo | Tempus Praesidium | --- | |
Phosphate | --- | 1~3 | Griseo | Tempus Praesidium) | --- |
Characteres corporei
Item | Morbi laoreet | Reference Precium | Unitas |
Auxiliaris Magnetic Properties | Reversible Temperature Coefficiens Of Br | -0.08--0.12 | %/ |
Reversible Temperature Coefficiens Of Hcj | -0.42~-0.70 | %/ | |
Imprimis Caloris | 0.104 | KJ·(Kg·℃)-1 | |
Curie Temperature | 310~ 380 | ℃ | |
Mechanica Physica Properties | Density | 7.5~7.80 | g/cm*3 |
Vickers duritia | 650 | Hv | |
Electrical Resistentia | 1.4x10-6 | μQ ·m | |
Compressive fortitudo | 1050 | MPa | |
Distrahentes fortitudo | 80 | Mpa | |
inflexio robur | 290 | Mpa | |
Scelerisque conductivity | 6~8.95 | W/m ·K | |
Modulus | 160 | GPa | |
Scelerisque Expansion (C⊥) | -1.5 | 10-6/℃-1 | |
Scelerisque Expansion (CII) | 6.5 | 10-6/℃-1 |